PPO GTX914

【基础创新塑料(美国)PPO GTX914】-《金红塑胶》长期现货供应PPO(聚苯醚）塑胶原料、玻纤增强PPO、耐高温PPO、耐化学PPO、PPO加工成型;专业渠道，专业团队，专业服务！只要你有需要，我们将用心与你沟通，竭诚为你服务！

产品说明:

NORYL GTX914 is an unfilled GTX grade with an ideal combination of impact performance, dimensional stability at elevated temperatures, chemical resistance and processability.

SABIC Innovative Plastics NORYL GTX GTX914 PPE+PA 物性表
物理性能	额定值 (公制)	额定值 (英制)	测试方法
比重	1.10 g/cc 	1.10 g/cc 	ASTM D792
密度	1.09 g/cc 	0.0394 lb/in3 	ISO 1183
水分吸收	1.20 % 	1.20 % 	23°C / 50% RH; ISO 62
饱和吸水率	3.5 % 	3.5 % 	ISO 62
线性成型收缩率,Flow	0.015 - 0.019 cm/cm 	0.015 - 0.019 in/in 	on Tensile Bar; SABIC Method
	0.013 - 0.016 cm/cm 
@Thickness 3.20 mm	0.013 - 0.016 in/in 
@Thickness 0.126 in	SABIC Method
线性成型收缩率，横向	0.011 - 0.014 cm/cm 
@Thickness 3.20 mm	0.011 - 0.014 in/in 
@Thickness 0.126 in	SABIC Method
熔体流动速率	12 g/10 min 
@Load 5.00 kg, Temperature 280 °C	12 g/10 min 
@Load 11.0 lb, Temperature 536 °F	ASTM D1238
化合物熔体指数	11 g/10 min 
@Load 5.00 kg, Temperature 280 °C	11 g/10 min 
@Load 11.0 lb, Temperature 536 °F	MVR [cm^3/10 min]; ISO 1133
机械性能	额定值 (公制)	额定值 (英制)	测试方法
硬度，H358/30	90.0 MPa 	13100 psi 	ISO 2039-1
抗张强度(断裂)	55.0 MPa 	7980 psi 	Type I, 50 mm/min; ASTM D638
	55.0 MPa 	7980 psi 	50 mm/min; ISO 527
抗张强度(屈服)	55.0 MPa 	7980 psi 	Type I, 50 mm/min; ASTM D638
	55.0 MPa 	7980 psi 	50 mm/min; ISO 527
伸长率 (断裂)	60 % 	60 % 	50 mm/min; ISO 527
	100 % 	100 % 	Type I, 50 mm/min; ASTM D638
屈服伸长率	7.5 % 	7.5 % 	50 mm/min; ISO 527
	15 % 	15 % 	Type I, 50 mm/min; ASTM D638
拉伸模量	1.95 GPa 	283 ksi 	50 mm/min; ASTM D638
	2.10 GPa 	305 ksi 	1 mm/min; ISO 527
弯曲强度	80.0 MPa 	11600 psi 	1.3 mm/min, 50 mm span; ASTM D790
	80.0 MPa 	11600 psi 	2 mm/min; ISO 178
弯曲模量	1.90 GPa 	276 ksi 	1.3 mm/min, 50 mm span; ASTM D790
	2.00 GPa 	290 ksi 	2 mm/min; ISO 178
悬壁梁缺口冲击强度	2.80 J/cm 	5.25 ft-lb/in 	ASTM D256
	1.20 J/cm 
@Temperature -30.0 °C	2.25 ft-lb/in 
@Temperature -22.0 °F	ASTM D256
	30.0 kJ/m2 	14.3 ft-lb/in2 	80*10*4; ISO 180/1A
	15.0 kJ/m2 
@Temperature -30.0 °C	7.14 ft-lb/in2 
@Temperature -22.0 °F	80*10*4; ISO 180/1A
简支梁缺口冲击强度	3.00 J/cm2 	14.3 ft-lb/in2 	Edgew 80*10*4 sp=62mm; ISO 179/1eA
	3.00 J/cm2 	14.3 ft-lb/in2 	ISO 179/2C
	1.50 J/cm2 
@Temperature -30.0 °C	7.14 ft-lb/in2 
@Temperature -22.0 °F	Edgew 80*10*4 sp=62mm; ISO 179/1eA
落锤总能量	60.0 J 
@Temperature 23.0 °C	44.3 ft-lb 
@Temperature 73.4 °F	ASTM D3763
泰伯磨损，毫克/1000次	15 	15 	CS-17, 1 kg; SABIC Method
电气性能	额定值 (公制)	额定值 (英制)	测试方法
介电常数	2.7 
@Frequency 1.00e+6 Hz	2.7 
@Frequency 1.00e+6 Hz	IEC 60250
	3.5 
@Frequency 50.0 - 60.0 Hz	3.5 
@Frequency 50.0 - 60.0 Hz	IEC 60250
介电强度	20.0 kV/mm 
@Thickness 3.20 mm	508 kV/in 
@Thickness 0.126 in	in oil; IEC 60243-1
耗散因数	0.024 
@Frequency 1.00e+6 Hz	0.024 
@Frequency 1.00e+6 Hz	IEC 60250
	0.072 
@Frequency 50.0 - 60.0 Hz	0.072 
@Frequency 50.0 - 60.0 Hz	IEC 60250
相比耐漏电起痕指数(CTI)	600 V 	600 V 	IEC 60112
热性能	额定值 (公制)	额定值 (英制)	测试方法
线形热膨胀系数 - 流动	90.0 μm/m-°C 
@Temperature -40.0 - 40.0 °C	50.0 μin/in-°F 
@Temperature -40.0 - 104 °F	ASTM E 831
	90.0 μm/m-°C 
@Temperature 23.0 - 60.0 °C	50.0 μin/in-°F 
@Temperature 73.4 - 140 °F	ISO 11359-2
线性热膨胀系数,横向流动	90.0 μm/m-°C 
@Temperature 23.0 - 60.0 °C	50.0 μin/in-°F 
@Temperature 73.4 - 140 °F	ISO 11359-2
	95.0 μm/m-°C 
@Temperature -40.0 - 40.0 °C	52.8 μin/in-°F 
@Temperature -40.0 - 104 °F	ASTM E 831
导热系数	0.230 W/m-K 	1.60 BTU-in/hr-ft2-°F 	ISO 8302
载荷下热变形温度(0.46 MPa)	180 °C 	356 °F 	Edgew 120*10*4 sp=100mm; ISO 75/Be
	180 °C 
@Thickness 3.20 mm	356 °F 
@Thickness 0.126 in	unannealed; ASTM D648
维卡软化温度	190 °C 	374 °F 	Rate B/50; ISO 306
	195 °C 	383 °F 	Rate B/120; ISO 306
	195 °C 	383 °F 	Rate B/50; ASTM D1525
	245 °C 	473 °F 	Rate A/50; ISO 306
可燃性(UL94)	HB 
@Thickness 1.60 mm	HB 
@Thickness 0.0630 in	UL 94 by SABIC-IP